Zhao Bo, Li Jing-wei, Li Shu-guang, Lu Yi-hui, Hao Ju-tao

Relationship between fracture toughness and temperature in epoxy coatings (in English)
Polimery 2015, No 4, 258


DOI: dx.doi.org/10.14314/polimery.2015.258

Summary
The fracture toughness KIC of nine kinds of epoxy coating specimens was tested in the temperature range from 20 to -40 °C, and the influence of temperature on KIC was discussed. The results showed that KIC decreases sharply in unmodified systems but increases for some specimens with 20—50 portions of rubber impact modifier. The elastic modulus test indicated that KIC is closely related with the modulus. Scanning Electron Microscopy images showed that the introduction of impact modifier to epoxy can enlarge the ductile deformation of the fracture surface. As aresult, the addition of rubber modifier is asuitable path to improve the anti-cracking performance of epoxy coatings at low temperature due to an increase of fracture toughness and reduction of elastic modulus, which thus can reduce the thermal stress in the process of cooling.

Keywords: epoxy resin, fracture toughness
e-mail: zhaobo@iwhr.com
Zhao Bo, Li Jing-wei, Li Shu-guang, Lu Yi-hui, Hao Ju-tao (895.1 KB)
Relationship between fracture toughness and temperature in epoxy coatings